Fracture Behavior of Welded Ductile Iron

In this study, fracture behavior of welded ductile iron was investigated experimentally and theoretically. Ferritic ductile irons were joined by cold arc welding method by using the nickel base electrode. In experimental part of the study, firstly, mechanical and metallographical properties of the welded specimens were identified. Then, J- Integral toughness values were determined by fracture toughness tests for different crack locations including base metal, heat affected zones and weld metal. In numerical part of the study, finite element analyses were conducted by fixing 3- D models precracked on different locations. After stress strain analyses, stress triaxiality and plastic deformation characteristics around crack tip were determined for each crack locations and different crack sizes. It was found that stress triaxiality and plastic strain values increase with growing crack length. Different regions with different strength levels, affect the extension of plastic deformation in the models. Hindrance on the extension of plastic deformation at HAZ and diffusion line causes extra increase in stress triaxiality at crack tip.

Autorentext

Dr. Hakan Çetinel was born in 1969 in Turkey and got his first degree in mechanical engineering in 1993 from Dokuz Eylul University, Turkey. He finished his PhD in metallurgical and materials engineering at Dokuz Eylul University, Turkey in 2004. He is now associate professor in mechanical engineering at Celal Bayar University, Turkey.