Metal-containing Hydrogenated Amorphous Carbon Thin Films

The growth and characteristics of metal containing amorphous hydrogenated carbon thin films (a-C:H/Me) were studied in this research. The discovery and the explanation of unprecedented self-assembled, alternating nano-layered structures are addressed. a- C:H/Me thin films were synthesized using one single target, a rotating but not revolving substrate, and constant feed gas compositions in a conventional reactive sputter deposition chamber. In order to explain the formation of the distinct structures, correlations were first made among the deposition rate, the composition, the crystallinity, the surface chemistry, and the microstructure of a- C:H/Me thin films. As a result, a processing window was obtained for the formation of the self- assembled, alternating nano-layered structures. It was found that such structures can be obtained under controlled growth parameters for selected metals. A growth mechanism based on the considerations of clustering of carbon and metal, segregation of carbon, catalytic effects of metal, formation of carbide, energy of adatoms, and surface diffusion of metal and carbon, has been developed.

Autorentext

Wan-Yu Wu was born in 1978 in Taipei, Taiwan and is currently a post doctor fellow at the National Cheng Kung University in the city of Tainan, Taiwan. Wu received both her BS and Ph.D. degrees from the Department of Materials Science and Engineering at the National Cheng Kung University.