Microstructure and Properties of Mg-Sn-Ca alloys with 3% Al additions

Technical demands for magnesium alloys are sufficient room, and elevated temperature mechanical properties, as well as corrosion resistance according to desired application. A new class of magnesium alloys based on the Mg-Sn system has been studied with many ternary alloying elements with emphasis on the Mg-Sn-Ca system due to their attractive property profile especially concerning creep resistance. This research work investigates the effect of 3 wt.% Al additions on two selected Mg- Sn-Ca alloys namely the Mg-3Sn-2Ca (TX32) alloy, and the Mg-9Sn-1Ca (TX91)alloy at different temper conditions, with the aim of improving room temperature mechanical properties, and corrosion resistance. A comparison of experimental results for the new Mg-Sn-Al-Ca (TAX) alloys, with their base Mg-Sn-Ca (TX) alloys, is performed, and explicitly discussed. The results showed enhanced hardening response in some of the alloys while the corrosion resistance deteriorated significantly. Al additions were found to have a favorable effect on strength of Mg-Sn-Ca(TX) alloys while they caused rapid decrease in their corrosion resistance.

Autorentext

Fady Refaat El-Sayed Ahmedfadooh4@yahoo.comBachelor of Science,Faculty of Engineering & Materials Science, German University in Cairo Currently: MSc. Student at GKSS Magnesium Innovations Center, Geesthacht, Germany